ʻO ka hui Perfluoroelastomer Pale Kemika Nui
Loaʻa ka laʻana waihona manuahi a loaʻa
Hāʻawi ʻo FUDI i ʻekolu ʻano operfluoroelastomer ffkmhui pū ʻia & polymer ffkm.
A. Loaʻa iā ia ka laulā wela hana ākea loa a me ke kūpaʻa ākea i nā pāpaho kemika.
Nā hiʻohiʻona
● Ke kūpaʻa koʻikoʻi i ka mahana kiʻekiʻe a hiki i ka 300-320 ℃
● Ke kūpaʻa koʻikoʻi i nā kemika hoʻouka kaua;
● Ke kūpaʻa mahu maikaʻi loa;
● Hoʻonohonoho ʻia ka hoʻopaʻa ʻana maikaʻi loa ʻoiai ma nā mahana kiʻekiʻe loa;
● Ka hiki ke hana ʻia e ka ʻenehana fluoroelastomer maʻamau ma nā lako laholio maʻamau.
● ʻO ke kumukūʻai ke kumu kūʻai nui loa.
Noi
ʻO nā apo-O, nā sila, nā diaphragms a me nā ʻāpana ʻē aʻe i hoʻohana ʻia i nā ʻoihana hana.
MOQ
300 grams
ʻIkepili no ka kuhikuhi ʻana
| Ke kū'ē wela | |
| Hoʻomehana i ka ʻelemakule 70 h @ 280 ℃ | |
| 100% Modulus Mpa | 9.5 |
| Ikaika tensile Mpa | 19.5 |
| Elongation i ka haki % | 215 |
| Kahakai Paʻakikī A | 72 |
| Hoʻomehana i ka ʻelemakule 70 h @ 300 ℃ | |
| 100% Modulus Mpa | 7.5 |
| Ikaika tensile Mpa | 17 |
| Elongation i ka haki % | 260 |
| Kahakai Paʻakikī A | 72 |
| Hoʻomehana i ka ʻelemakule 70 h @ 316 ℃ | |
| 100% Modulus Mpa | 6.5 |
| Ikaika tensile Mpa | 14 |
| Elongation i ka haki % | 320 |
| Kahakai Paʻakikī A | 72 |
B. He palena ko ka pae mahana hana a me ke kū'ē ākea loa i nā pāpaho kemika.
Nā hiʻohiʻona
● Ke kūpaʻa koʻikoʻi i ka mahana kiʻekiʻe a hiki i 250 ~ 260 ℃
● Ke kūpaʻa koʻikoʻi i nā kemika hoʻouka kaua;
● Ke kūpaʻa mahu maikaʻi loa;
● Hoʻonohonoho ʻia ka hoʻopaʻa ʻana maikaʻi loa ʻoiai ma nā mahana kiʻekiʻe loa;
● ʻOi aku ka haʻahaʻa o ke kumukūʻai ma mua o ka papa A.
Noi
ʻO nā apo-O, nā sila, nā diaphragms a me nā ʻāpana ʻē aʻe i hoʻohana ʻia i nā wahi ʻino.
MOQ
300 grams
ʻIkepili no ka kuhikuhi ʻana
| Kahakai Paʻakikī A | 74 |
| Ka umekaumaha / | 1.99 |
| Ikaika tensile Mpa | 24.5 |
| 100% Modulus Mpa | 7.5 |
| % Hoʻolōʻihi | 200 |
| Hoʻonohonoho ʻia ka hoʻopaʻa ʻana he 72 h @ 200 ℃ | 18.1 |
| Hoʻonohonoho ʻia ka hoʻopaʻa ʻana he 72 h @ 230 ℃ | 26.7 |
Ke kū'ē kemika (No Ketone, Ester, Ether)
| Kemika | Mahana | Hoʻololi ma hope o 168 hola (%) | Hoʻololi ma hope o 500 hola (%) |
| ʻAsetona | 40℃ | 2.5 | 3.3 |
| ʻO ka methyl ethyl ketone | 2.2 | 3.2 | |
| ʻIsoforone | 0.1 | 0.5 | |
| ʻEtila ʻaseta | 3.1 | 3.8 | |
| ʻO Dioxane | 1.2 | 2.0 | |
| ʻO ka methyl isobutyl ketone | 1.2 | 2.0 | |
| ʻAsetilasetona | 0.8 | 1.3 | |
| ʻO ka buthyl acetate | 1.5 | 2.5 | |
| ʻEtera diethyl | 25℃ | 2.6 | 4.3 |
C. He palena iki kona pae mahana hana a me ke kūpaʻa maikaʻi i nā pāpaho kemika.
Nā hiʻohiʻona
● Ke kūpaʻa maikaʻi loa i ka mahana kiʻekiʻe a hiki i ka 240 ℃
● Ke kūpaʻa koʻikoʻi i nā kemika hoʻouka kaua;
● Ke kūpaʻa mahu maikaʻi loa;
● Hoʻonohonoho ʻia ka hoʻopaʻa ʻana maikaʻi loa ʻoiai ma nā mahana kiʻekiʻe loa;
● Ka hiki ke hana ʻia e ka ʻenehana fluoroelastomer maʻamau ma nā lako laholio maʻamau.
● ʻO ke kumukūʻai haʻahaʻa loa.
ʻIkepili no ka kuhikuhi ʻana
| Ka ʻelemakule ʻana o ka ea wela | 300℃×24Hrs | GB/T 3512-2014 | |||
| Ikaika tensile | % | -18.1 | |||
| Hoʻolōʻihi | % | 17.1 | |||
| Hoʻololi paʻakikī | 0.2 | ||||
| Hoʻonohonoho hoʻopili | 23℃×70Hrs | GB/T 7759.1-2015 | |||
| Hoʻonohonoho hoʻopili | % | 11.2 | |||
| Hoʻonohonoho hoʻopili | 204℃×70Hrs | GB/T 7759.1-2015 | |||
| Hoʻonohonoho hoʻopili | % | 22.7 | |||
| Hoʻonohonoho hoʻopili | 250℃×70Hrs | GB/T 7759.1-2015 | |||
| Hoʻonohonoho hoʻopili | % | 33.2 | (Aia nā māwae) | ||
| ʻO Fule RP-3 | 150℃×24Hrs | GB/T 1690-2010 | |||
| Ikaika tensile | % | -14.3 | |||
| Hoʻolōʻihi | % | 5.8 | |||
| Hoʻololi paʻakikī | -2 | ||||
| Hoʻololi leo | % | 4.6 | |||
| Haʻahaʻa ka mahana | GB/T 15256-2014 | ||||
| Mahana palupalu | ℃ | -30 |